GOMBÁR, Miroslav, Ján KMEC, Miroslav BADIDA, Lýdia SOBOTOVÁ, Alena VAGASKÁ and A. BADIDOVÁ. ANALYSIS OF PHYSICAL FACTORS ON CHOSEN PROPERTIES OF ANODIC ALUMINA OXIDE (AAO) LAYERS AND ENVIRONMENT. Metalurgija. Zagreb: Hrvatsko metalurško društvo (HMD) - Croatia Metallurgical Society (CMS), roč. 55, No 4, p. 799-802. ISSN 0543-5846. 2016.
Other formats:   BibTeX LaTeX RIS
Basic information
Original name ANALYSIS OF PHYSICAL FACTORS ON CHOSEN PROPERTIES OF ANODIC ALUMINA OXIDE (AAO) LAYERS AND ENVIRONMENT
Name in Czech Analýza fyzikálních faktorů na vybrané charakteristiky anodického oxidu hlinitého (AAO) vrstev a životní prostředí
Authors GOMBÁR, Miroslav (703 Slovakia, belonging to the institution), Ján KMEC (703 Slovakia, belonging to the institution), Miroslav BADIDA (703 Slovakia), Lýdia SOBOTOVÁ (703 Slovakia), Alena VAGASKÁ (703 Slovakia) and A. BADIDOVÁ (703 Slovakia).
Edition Metalurgija, Zagreb, Hrvatsko metalurško društvo (HMD) - Croatia Metallurgical Society (CMS), 2016, 0543-5846.
Other information
Original language English
Type of outcome Article in a journal
Field of Study 20400 2.4 Chemical engineering
Country of publisher Croatia
Confidentiality degree is not subject to a state or trade secret
RIV identification code RIV/75081431:_____/16:00000667
Organization unit Institute of Technology and Business in České Budějovice
UT WoS 000376167100059
Keywords (in Czech) Eloxování hliníku; mikrotvrdost; vrstva; tloušťky; životní prostředí
Keywords in English Anodizing of aluminium; microhardness; layer; thickness; environment
Tags IF, KSTR5, RIV16, SCOPUS
Tags Reviewed
Changed by Changed by: Hana Dlouhá, učo 19800. Changed: 2/9/2016 10:23.
Abstract
In the contribution is evaluated an impact of physical factors of anodizing process, namely the temperature of an electrolyte, anodizing time and voltage, on the change of values of Vickers microhardness and thickness of formed layer of experimental materials Al99-5. By increasing of electrolyte temperature, the values of layer microhardness and thickness layer increase, namely about 0.78 % at the increasing of electrolyte temperature by 1 °C. By lengthening of anodizing time grows the value of layer thickness, but only to the value of the critical deposition time, when chemical dissolution of the layer start to be more prominent. By voltage increasing, values of layer thickness and micro-hardness are increased in the range of the used experimental values.
Abstract (in Czech)
V příspěvku je hodnocen vliv fyzikálních faktorů eloxování, a to sice na teplotu elektrolytu, času eloxování a napětí, na změnu hodnot Vickersovy mikrotvrdosti a tloušťka vytvořené vrstvy experimentálních materiálů Al99-5. Zvýšením teploty elektrolytu, hodnoty vrstvy mikrotvrdosti a zvýšení tloušťky vrstvy, a to o 0,78 %, při zvyšování teploty elektrolytu o 1 ° C. O prodloužení doby eloxování roste hodnota tloušťky vrstvy, ale pouze na hodnotu kritické době, kdy depozice, chemické rozpuštění začátku vrstvy byla výraznější. Zvýšením napětí, hodnoty tloušťky vrstvy a mikro-tvrdosti jsou v rozsahu použitých experimentálních hodnot zvýšeny.