J 2020

The use of concentrated heat stream to repair AlZn10Si8Mg alloy castings

M., Tupaj, Trytek A., Łysiak K., Zbyrad-Kołodziej W., Łaczek A. et. al.

Basic information

Original name

The use of concentrated heat stream to repair AlZn10Si8Mg alloy castings

Name in Czech

Použití koncentrovaného proudu tepla k opravě odlitků ze slitin AlZn10Si8Mg

Authors

M., Tupaj (616 Poland, guarantor), Trytek A. (616 Poland), Łysiak K. (616 Poland), Zbyrad-Kołodziej W. (616 Poland), Łaczek A. (616 Poland) and Ján MAJERNÍK (703 Slovakia, belonging to the institution)

Edition

Manufacturing Technology, Usti nad Labem, J. E. Purkyne University in Usti nad Labem, 2020, 1213-2489

Other information

Language

English

Type of outcome

Článek v odborném periodiku

Field of Study

20300 2.3 Mechanical engineering

Country of publisher

Czech Republic

Confidentiality degree

není předmětem státního či obchodního tajemství

References:

RIV identification code

RIV/75081431:_____/20:00001807

Organization unit

Institute of Technology and Business in České Budějovice

Keywords (in Czech)

Al slitina; Počítačová tomografie; Koncentrovaný proud tepla; Vady odlitků; Metalografické testy

Keywords in English

Al alloy; Computer tomography; Concentrated heat stream; Defects in castings; Metallographic tests

Tags

Změněno: 6/10/2020 11:19, Kateřina Nygrýnová

Abstract

V originále

The present paper discusses the possibility to use three different sources of concentrated heat stream to repair superficial defects on AlZn10Si8Mg alloy castings. Simulated defects were prepared on specimens taken from a production casting made with the use of low-pressure casting method. The energy sources used to repair the defect were those known as MIG/MAG, TIG, and ML (micro-laser) methods. As the filler, a AlSi5 welding wire was used. The quality of repair was assessed based on both destructive and non-destructive testing. To evaluate porosity of the performed overlay welds, the computer X-ray tomography technique was employed. Metallographic examination was used to assess macro-and micro-structure of overlay welds, measure geometrical parameters of the welds and the heat-affected zone, and determine values of SDAS microstructure parameter. Hardness of overlay welds and the casting material was measured with the use of Brinell hardness machine.

In Czech

Tato práce pojednává o možnosti použít tři různé zdroje koncentrovaného proudu tepla k opravě povrchových defektů na slitinových odlitcích AlZn10Si8Mg. Simulované vady byly připraveny na vzorcích odebraných z výrobního odlitku vyrobeného metodou nízkotlakého odlévání. K opravě defektu byly použity zdroje energie známé jako metody MIG / MAG, TIG a ML (mikro-laser). Jako plnivo byl použit svařovací drát AlSi5. Kvalita opravy byla hodnocena na základě destruktivního i nedestruktivního testování. K vyhodnocení pórovitosti provedených svarových svarů byla použita technika počítačové rentgenové tomografie. Metalografické vyšetření bylo použito k posouzení makrostruktury a mikrostruktury svarů, měření geometrických parametrů svarů a tepelně ovlivněné zóny a stanovení hodnot parametru mikrostruktury SDAS. Tvrdost svarů a odlévaného materiálu byla měřena pomocí tvrdoměru Brinell.