J 2016

ANALYSIS OF PHYSICAL FACTORS ON CHOSEN PROPERTIES OF ANODIC ALUMINA OXIDE (AAO) LAYERS AND ENVIRONMENT

GOMBÁR, Miroslav, Ján KMEC, Miroslav BADIDA, Lýdia SOBOTOVÁ, Alena VAGASKÁ et. al.

Basic information

Original name

ANALYSIS OF PHYSICAL FACTORS ON CHOSEN PROPERTIES OF ANODIC ALUMINA OXIDE (AAO) LAYERS AND ENVIRONMENT

Name in Czech

Analýza fyzikálních faktorů na vybrané charakteristiky anodického oxidu hlinitého (AAO) vrstev a životní prostředí

Authors

GOMBÁR, Miroslav (703 Slovakia, belonging to the institution), Ján KMEC (703 Slovakia, belonging to the institution), Miroslav BADIDA (703 Slovakia), Lýdia SOBOTOVÁ (703 Slovakia), Alena VAGASKÁ (703 Slovakia) and A. BADIDOVÁ (703 Slovakia)

Edition

Metalurgija, Zagreb, Hrvatsko metalurško društvo (HMD) - Croatia Metallurgical Society (CMS), 2016, 0543-5846

Other information

Language

English

Type of outcome

Článek v odborném periodiku

Field of Study

20400 2.4 Chemical engineering

Country of publisher

Croatia

Confidentiality degree

není předmětem státního či obchodního tajemství

RIV identification code

RIV/75081431:_____/16:00000667

Organization unit

Institute of Technology and Business in České Budějovice

UT WoS

000376167100059

Keywords (in Czech)

Eloxování hliníku; mikrotvrdost; vrstva; tloušťky; životní prostředí

Keywords in English

Anodizing of aluminium; microhardness; layer; thickness; environment

Tags

Tags

Reviewed
Změněno: 2/9/2016 10:23, Hana Dlouhá

Abstract

ORIG CZ

V originále

In the contribution is evaluated an impact of physical factors of anodizing process, namely the temperature of an electrolyte, anodizing time and voltage, on the change of values of Vickers microhardness and thickness of formed layer of experimental materials Al99-5. By increasing of electrolyte temperature, the values of layer microhardness and thickness layer increase, namely about 0.78 % at the increasing of electrolyte temperature by 1 °C. By lengthening of anodizing time grows the value of layer thickness, but only to the value of the critical deposition time, when chemical dissolution of the layer start to be more prominent. By voltage increasing, values of layer thickness and micro-hardness are increased in the range of the used experimental values.

In Czech

V příspěvku je hodnocen vliv fyzikálních faktorů eloxování, a to sice na teplotu elektrolytu, času eloxování a napětí, na změnu hodnot Vickersovy mikrotvrdosti a tloušťka vytvořené vrstvy experimentálních materiálů Al99-5. Zvýšením teploty elektrolytu, hodnoty vrstvy mikrotvrdosti a zvýšení tloušťky vrstvy, a to o 0,78 %, při zvyšování teploty elektrolytu o 1 ° C. O prodloužení doby eloxování roste hodnota tloušťky vrstvy, ale pouze na hodnotu kritické době, kdy depozice, chemické rozpuštění začátku vrstvy byla výraznější. Zvýšením napětí, hodnoty tloušťky vrstvy a mikro-tvrdosti jsou v rozsahu použitých experimentálních hodnot zvýšeny.