Effect of electrolyte temperature on the thickness of anodic aluminium oxide (AAO) layer

MICHAL, Peter, Alena VAGASKÁ, Erika FECHOVÁ, Miroslav GOMBÁR, Dražan V. KOZAK et. al.

Basic information

Original name

Effect of electrolyte temperature on the thickness of anodic aluminium oxide (AAO) layer

Name in Czech

Vliv teploty elektrolytu na tloušťku vrstvy anodického oxidu hlinitého (AAO)

Authors

MICHAL, Peter (703 Slovakia, belonging to the institution), Alena VAGASKÁ (703 Slovakia), Erika FECHOVÁ (703 Slovakia), Miroslav GOMBÁR (703 Slovakia, belonging to the institution) and Dražan V. KOZAK (191 Croatia)

Edition

Metalurgija, Zagreb, Hrvatsko metalurško društvo (HMD) - Croatia Metallurgical Society (CMS), 2016, 0543-5846

Other information

Language

English

Type of outcome

Článek v odborném periodiku

Field of Study

10405 Electrochemistry

Country of publisher

Croatia

Confidentiality degree

není předmětem státního či obchodního tajemství

RIV identification code

RIV/75081431:_____/16:00000627

Organization unit

Institute of Technology and Business in České Budějovice

Keywords (in Czech)

anodický oxid hlinitý (AAO); tloušťka vrstvy; elektrolyt; teplota; oxidace

Keywords in English

anodic aluminium oxide (AAO); layer thickness; electrolyte; temperature; oxidation

Tags

Tags

Reviewed
Změněno: 2/9/2016 10:23, Hana Dlouhá

Abstract

V originále

Effect of electrolyte temperature on the thickness of resulting oxide layer has been studied. Unlike previous published studies this article was aimed to monitor the relationship between electrolyte temperature and resulting AAO layer thickness in interaction with other input factors affecting during anodizing process under special process condition, i.e. lower concentration of sulphuric acid, oxalic acid, boric acid and sodium chloride. According to Design of Experiments (DOE) 80 individual test runs of experiment were carried out. Using statistical analysis and artificial intelligence for evaluation, the computational model predicting the thickness of oxide layer in the range from 5 / micrometers to 15 / micrometers with tolerance ± 0,5 / micrometer was developed.

In Czech

Byl zkoumán vliv teploty elektrolytu na tloušťku výsledné vrstvy oxidu. Na rozdíl od předchozích publikovaných studií, bylo cílem tohoto článku sledovat vztah mezi teplotou elektrolytu a výslednou AAO tloušťkou vrstvy v interakci s jinými vstupními faktory ovlivňující během procesu eloxování pod podmínkou zvláštního procesu, tedy nižší koncentrace kyseliny sírové, kyseliny šťavelové, kyseliny borité a chloridu sodného. Podle návrhu experimentů (DOE) 80 byly provedeny jednotlivé zkušební experimenty. Pomocí statistické analýzy a umělé inteligence pro hodnocení, výpočetní model předpovídá tloušťku vrstvy oxidu v rozmezí od 5 / mikrometrů až 15 / mikrometrů s tolerancí ± 0,5 / mikrometru.