The paper deals with evaluation of quality of electrolytic coating by statistical methods. Electrolytic solution was created by ZnCl2 within interval of 0,062 mol.l-1 to 1,01 mol.l-1, NaCl ranging from 7,01 mol.l-1 to 60,66 mol.l-1, H3BO3 ranging from 0,11 mol.l-1 to 0,89 mol.l-1. Physical conditions of the experiment are represented by the electrolyte temperature ranging from - 3,78 °C to 43,78 °C, electroplating period ranging from 3,11 to 26,98 min and voltage ranging from 1,62 V to 6,38 V. Steel S355J0 was used as an experimental material. The results showed that zinc chloride volume contained in the electrolyte does not produce any influence on resulting quality of zinc coating.
In Czech
Článek se zabývá hodnocením kvality elektrolytické potahování pomocí statistických metod. Elektrolytický roztok se vytvořil ZnCl2 v intervalu 0,062 mol.l-1 až 1,01 mol.l-1, NaCl v rozsahu od 7,01 mol.l-1 na 60,66 mol.l-1, H3BO3 od 0,11 mol.l-1 0,89 mol.l-1. Fyzikální podmínky experimentu jsou shrnuty v elektrolytu teplotě v rozmezí od - 3,78 ° C na 43,78 ° C, galvanické období v rozmezí od 3,11 do 26,98 min a napětí v rozmezí od 1,62 do 6,38 V. V oceli S355J0 byl používán jako pokusného materiálu. Výsledky ukázaly, že chlorid zinečnatý objem obsažený v elektrolytu neprodukuje žádný vliv na výslednou kvalitu zinkového povlaku.