Effect of the Electrolyte Temperature and the Current Density on a Layer Microhardness Generated by the Anodic Aluminium Oxidation
SPIŠÁK, Emil, Miroslav GOMBÁR, Ján KMEC, Alena VAGASKÁ, Erika FECHOVÁ et. al.
Basic information
Original name
Effect of the Electrolyte Temperature and the Current Density on a Layer Microhardness Generated by the Anodic Aluminium Oxidation
Name in Czech
Vliv teploty elektrolytu a aktuálni hustoty na mikrotvrdost vrstvy generované anodickou oxidaci hliníku
Authors
SPIŠÁK, Emil (703 Slovakia, guarantor), Miroslav GOMBÁR (703 Slovakia, belonging to the institution), Ján KMEC (703 Slovakia, belonging to the institution), Alena VAGASKÁ (703 Slovakia), Erika FECHOVÁ (703 Slovakia), Peter MICHAL (703 Slovakia), Ján PITEL (703 Slovakia) and Daniel KUČERKA (703 Slovakia, belonging to the institution)
Edition
ADVANCES IN MATERIALS SCIENCE AND ENGINEERING, New York, HINDAWI PUBLISHING CORPORATION, 2015, 1687-8434
Other information
Type of outcome
Článek v odborném periodiku
Field of Study
10405 Electrochemistry
Country of publisher
United States of America
Confidentiality degree
není předmětem státního či obchodního tajemství
RIV identification code
RIV/75081431:_____/15:00000474
Organization unit
Institute of Technology and Business in České Budějovice
Keywords (in Czech)
Teplota elektrolytu; Hustota elektrolytu; Mikrotvrdost vrstvy; Anodická oxidace hliníka
Keywords in English
The temperature of the electrolyte; The density of the electrolyte; Microhardness laye; The Anodic Aluminium Oxidation
V originále
The paper investigates the influence of the chemical composition and temperature of electrolyte, the oxidation time, voltage, and the current density on Vickers microhardness of aluminium oxide layers, at the same time.The layers were generated in the electrolytes with different concentrations of sulphuric and oxalic acids and surface current densities 1Axdm-2, 3Axdm-2, and 5Axdm-2. The electrolyte temperature varied from -1.78°C to 45.78°C. The results have showed that while increasing the electrolyte temperature at the current density of 1Axdm-2, the increase in the layer microhardness values is approximately by 66%. While simultaneously increasing themolar concentration ofH2SO4 in the electrolyte, the growth rate of the microhardness value decreases. At the current density of 3Axdm-2, by increasing the electrolyte temperature, a reduction in the microhardness of the generated layer occurs with the anodic oxidation time less than 25 min. The electrolyte temperature is not significant with the changing values of the layer microhardness at voltages less than 10.5V.
In Czech
Článek zkoumá vliv chemického složení a teplotu elektrolytu, čas oxidace, napětí, a proudové hustoty na Vickersově mikrotvrdosti vrstev oxidu hlinitého, při stejných časových úsecích. Vrstvy byly vygenerovány v elektrolytech s různými koncentracemi kyseliny sírové a šťavelové kyseliny a povrchové proudové hustoty 1Axdm-2, 3Axdm-2, a 5Axdm-2. Teplota elektrolytu se pohybovala od -1.78°C do 45.78°C. Výsledky ukázaly, že se při zvýšení teploty elektrolytu, při proudové hustotě 1Axdm-2, zvýšení mikrotvrdosti hodnot vrstvy je přibližně o 66%. Zatímco současně zvyšující se molární koncentrace H2SO4 v elektrolytu, tempo růstu hodnoty mikrotvrdosti klesá. Na proudové hustotě 3Axdm-2, zvýšením teploty elektrolytu, snížení mikrotvrdosti generovaného vrstvy dochází s časem anodickou oxidaci menší než 25 min. Teplota elektrolytu není významné s měnícími se hodnotami vrstvy mikrotvrdosti při napětí nižší než 10,5 V.